S45C Carbon Steel | 760 Carbon Steel | AISI 1045 | EN9 Steel
E Steel SDN BHD is Malaysia steel supplier / stockist / Metal B2B Platform and Marketplace which supply a wide range of Carbon Steel Sheets , Carbon Steel Round Bar and Rod, Carbon Steel Plate from ASTM A36 , 760 Steel Plate and rod , A105 Carbon Steel , etc.
Our spirit is to help the local SMEs on the sourcing of different steels and metal with no minimum order (NO MOQ).
We have over 100 Tons of Carbon Steel Round Bar ranging from DIA 16mm to DIA 760mm ready to fulfill the market demands to the General Engineering Industry , Palm Oil Industry , etc.
Grades : ASTM A105 , S45C , S50C , AISI 4140 (709 Steel Equivalent), AISI 4340 (705 Steel Equivalent), AISI 4130, 5919, 6587
Carbon Steel AISI 1045 is a medium tensile low hardenability carbon steel generally supplied in the cold drawn or turned and polished condition, with a typical tensile strength range 600 – 950 Mpa and Brinell hardness range 179 – 280. in either condition.
Characterised by good strength and impact properties, with good machinability and reasonable weldability in the as supplied condition.
Material S45C has a low through hardening capability with sections up to around 60mm only generally recommended as suitable for through hardening and tempering. It can however be successfully flame or induction hardened in the as supplied condition resulting in surface hardnesses of up to Rc 54 – Rc 60 depending upon quenching medium employed, type of set up, section size etc. Core strengths will remain as supplied.
It does not however respond satisfactorily to nitriding due to a lack of suitable alloying elements.
EN9 is used extensively by all industry sectors for applications requiring more strength and wear resistance than the low carbon mild steels can provide and the higher strength of the low alloy high tensile steels is not necessary, plus those applications requiring flame or induction hardening.
Do not forge below 850 oC
Finished forgings may be air cooled.
Following quenching to hand warm, most components should be tempered at 150 oC – 200 oC to remove quenching stresses in the case. This will have little effect on case hardness.
or:Heat to 830 oC – 860 oC soak as above and quench in oil.Temper immediately while still hand warm.
Cool in still air.
We ensure every packing of our material sending out from E Steel warehouse is nice and secure
Our spirit is to help the local SMEs on the sourcing of different steels and metal with no minimum order (NO MOQ).
We have over 100 Tons of Carbon Steel Round Bar ranging from DIA 16mm to DIA 760mm ready to fulfill the market demands to the General Engineering Industry , Palm Oil Industry , etc.
Grades : ASTM A105 , S45C , S50C , AISI 4140 (709 Steel Equivalent), AISI 4340 (705 Steel Equivalent), AISI 4130, 5919, 6587
AISI 1045 Carbon Steel Suppliers - S45C , 760 Carbon Steel Equivalent , 1.1191 , EN9 , CK45
Carbon Steel AISI 1045 is a medium tensile low hardenability carbon steel generally supplied in the cold drawn or turned and polished condition, with a typical tensile strength range 600 – 950 Mpa and Brinell hardness range 179 – 280. in either condition.
Characterised by good strength and impact properties, with good machinability and reasonable weldability in the as supplied condition.
Material S45C has a low through hardening capability with sections up to around 60mm only generally recommended as suitable for through hardening and tempering. It can however be successfully flame or induction hardened in the as supplied condition resulting in surface hardnesses of up to Rc 54 – Rc 60 depending upon quenching medium employed, type of set up, section size etc. Core strengths will remain as supplied.
It does not however respond satisfactorily to nitriding due to a lack of suitable alloying elements.
EN9 is used extensively by all industry sectors for applications requiring more strength and wear resistance than the low carbon mild steels can provide and the higher strength of the low alloy high tensile steels is not necessary, plus those applications requiring flame or induction hardening.
Carbon Steel S45C Specifications
| DIN | AISI | JIS | Chemical Composition | |||||||||||
| C | Si | Mn | P | S | Co | Cr | Mo | Ni | V | W | Cu | |||
| CK45 | 1045 | S45C | 0.42 to 0.48 | 0.20 to 0.35 | 0.60 to 0.90 | < 0.030 | < 0.035 | – | – | – | – | – | – | – |
Mechanical Properties of 760 Carbon Steel - Hot Rolled Condition
| Tensile Strength Mpa | Yield Strength Mpa | Elongation In 50mm % | Hardness Brinell HB |
| 570 – 700 | 300 – 450 | 14 – 30 | 170 – 210 |
Mechanical Properties of EN9 Steel – Normalised Condition
| Tensile Strength Mpa | Yield Strength Mpa | Elongation in 50mm % | Impact Izod J | Hardness | |||
| HB | Rc | ||||||
| 640 | 410 | 22 | 54 | 187 | 10 | ||
Forging
Pre heat to 750 oC – 800 oC, then continue heating to 1100 oC – 1200 oC maximum, hold until temperature is uniform throughout the section and commence forging immediately.Do not forge below 850 oC
Finished forgings may be air cooled.
Heat Treatment of AISI 1045 Carbon Steel
Annealing
Heat to 800 oC – 850 oC hold until temperature is uniform throughout the section, and cool in furnace.Flame or Induction Hardening
Heat as quickly as possible to the austenitic temperature range (820 oC – 860 oC) and required case depth followed by an immediate water or oil quench, depending upon hardness required, workpiece size/shape and quenching arrangements.Following quenching to hand warm, most components should be tempered at 150 oC – 200 oC to remove quenching stresses in the case. This will have little effect on case hardness.
Hardening of CK45 Steel
Heat to 820 oC – 850 oC hold until temperature is uniform throughout the section, soak for 10 – 15 minutes per 25mm of section, and quench in water or brine.or:Heat to 830 oC – 860 oC soak as above and quench in oil.Temper immediately while still hand warm.
Carbon Steel S45C steel- Normalizing
Heat to 870 oC – 920 oC hold until temperature is uniform throughout the section, soak for 10 – 15 minutes.Cool in still air.
Stress Relieving
Heat to 550 oC – 660 oC hold until temperature is uniform throughout the section, soak for 1 hour per 25mm of section, and cool in still air.S45C steel Tempering
Re heat to 400 oC – 650 oC as required, hold until temperature is uniform throughout the section, soak for 1 hour per 25mm of section, and cool in still air.Machining of 1.1191 Medium Carbon Steel
1.1191 carbon steel in the cold drawn or turned and polished condition has very good machinability and all operations such as turning, drilling, broaching, milling and tapping etc. can be carried out satisfactorily using machine manufacturers recommendations for suitable tool type, feeds and speeds.S45C | AISI 1045 Carbon Steel Round Bar Suppliers Indonesia
E Steel supplys and exports 4tons of Carbon Steel AISI 1045, S45C , C45 Round Bars to Indonesia by Ocean FreightWe ensure every packing of our material sending out from E Steel warehouse is nice and secure
Our Sales & Supplier Network
Australia, Pakistan, Malaysia, Singapore, Taiwan, China,Vietnam, Belgium, Japan, South Korea, Philippines, France, United Kingdom, Indonesia, Thailand, Hong Kong, China, Sweden, United States, Dubai, Finland, Brunei,Germany.
E Steel is a Global Metal Procurement Company in providing and sourcing raw materials to the wide range of engineering industries / sectors. We works as the the Online B2B Metal Marketplace to help our customers in finding the special steels that might feel hard to source locally.