Beryllium Copper C17200 , BECU C17200 Rod, Plate, Strip, Coil
We are the Beryllium Copper C17200 Supplier Malaysia , Singapore and Indonesia
We export to Singapore , Indonesia , Brunei and other ASEAN Countries with no MOQ.
E Steel supply BeCu Beryllium Copper in Round Bars (Rods & Shafts) , Beryllium Copper Plates , Coils and Strips.
These copper alloys are mainly used for applications that required high strength, stiffness and good conductivity.
The tensile strength of C17200 Beryllium Copper is over 1380MPA (200ksi)
Machinability : The machinability rate for C17200 Beryllium Copper is 20%
Welding : Welding procedures such as butt welding, seam welding, spot welding, coated metal arc welding, gas shielded arc welding, brazing and soldering are recommended for BeCu C17200.
However, oxyacetylene welding is not recommended.
Forging : Forging of C17200 Beryllium Copper is carried out at temperature ranging from 649°C - 816°C
Hot & Cold Working : Beryllium Copper has good hot working property and cold working property.
Annealing : C17200 Beryllium Copper is annealed at the temperature from 774°C - 802°C
Our Sales & Supplier Network
We export to Singapore , Indonesia , Brunei and other ASEAN Countries with no MOQ.
E Steel supply BeCu Beryllium Copper in Round Bars (Rods & Shafts) , Beryllium Copper Plates , Coils and Strips.
Beryllium Copper C17200 Suppliers - C17200 Copper , BeCu
BeCu Beryllium Copper C17200 are copper alloys that are ductile and produced in mill hardened and heat treatable tempers.These copper alloys are mainly used for applications that required high strength, stiffness and good conductivity.
The tensile strength of C17200 Beryllium Copper is over 1380MPA (200ksi)
Chemical Composition (%) of BeCu C17200
This table will show the chemical composition of C17200 Copper Alloys -| Elements | Content (%) |
| Cu | 97.9 |
| Be | 1.9 |
| Co | 0.20 |
Mechanical Properties of Beryllium Copper C17200
| Properties | Metric | Imperial |
| Hardness (Rockwell B) | 80.0 - 85.0 | 80.0 - 85.0 |
| Tensile Strength , | 1280 - 1480 MPa | 186,000 - 215,000 psi |
| Yield Strength | 965 - 1205 MPa | 140,000 - 174,800 psi |
| Elongation at break | 15 - 30% | 15 - 30% |
| Modulus of elasticity | 125 - 130 GPa | 18,100 - 18,900 ksi |
| Poissos ratio | 0.300 | 0.300 |
| Machinability (UNS C63000 = 100%) | 20% | 20% |
| Shear Modulus | 50 GPa | 7250 ksi |
Fabrication and Heat Treatment for BeCu
Machinability : The machinability rate for C17200 Beryllium Copper is 20% Welding : Welding procedures such as butt welding, seam welding, spot welding, coated metal arc welding, gas shielded arc welding, brazing and soldering are recommended for BeCu C17200.
However, oxyacetylene welding is not recommended.
Forging : Forging of C17200 Beryllium Copper is carried out at temperature ranging from 649°C - 816°C
Hot & Cold Working : Beryllium Copper has good hot working property and cold working property.
Annealing : C17200 Beryllium Copper is annealed at the temperature from 774°C - 802°C
Fabrication and Heat Treatment for BeCu
There are some major applications for Beryllium Copper C17200 , such as :- Electrical / Electronic Connectors
- Current-carrying springs
- Precision Screw Machined Parts
- Welding Electrodes
- Bearings
- Plastic Moulds
- Corrosion Resistant Components
Our Sales & Supplier Network
Australia, Pakistan, Malaysia, Singapore, Taiwan, China,Vietnam, Belgium, Japan, South Korea, Philippines, France, United Kingdom, Indonesia, Thailand, Hong Kong, China, Sweden, United States, Dubai, Finland, Brunei,Germany.
E Steel is a Global Metal Procurement Company in providing and sourcing raw materials to the wide range of engineering industries / sectors. We works as the the Online B2B Metal Marketplace to help our customers in finding the special steels that might feel hard to source locally.