Stainless Steel SS410 is the basic martensitic stainless steel; like most non-stainless steels it can be hardened by a “quench-and-temper” heat treatment.
Our specialty is to provide wide range of stainless steel with no minimum order (MOQ).
E Steel supply Stainless Steel SUS410 (SS410) Round Bars / Rods / Shaft , SUS410 (SS410) Plates with origin Germany and Japan.
Martensitic stainless steels are optimised for high hardness, and other properties are to some degree compromised. Fabrication must be by methods that allow for poor weldability and usually the need for a final heat treatment. Corrosion resistance of the martensitic grades is lower than that of the common austenitic grades, and their useful operating temperature range is limited by their loss of ductility at sub-zero temperatures and loss of strength by over-tempering at elevated temperatures.
* Annealed properties are specified for Condition A of ASTM A276, for cold finished bar.
# Due to associated low impact resistance this steel should not be tempered in the range 425-600°C
* These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted.
410 Stainless Steel resists dry atmosphere, fresh water, mild alkalies and acids, food, steam and hot gases. Must be hardened for maximum heat and corrosion resistance. Performance is best with a smooth surface finish. Less corrosion resistant than the austenitic grades and also less than 17% chromium ferritic alloys such as Grade 430.
Good resistance to scaling up to approximately 650°C, but generally not recommended for use in temperatures between 400 and 580°C, because of the reduction in mechanical properties.
Hardening – Hardening of grade 410 steels can be performed at 925 to 1010 °C, followed by air and oil quenching. Heavy sections of grade 410 need to be oil quenched. Tempering, to enhance the mechanical properties and hardness of grade 410 steels, follows this process. It is not recommended to perform tempering at temperatures from 400 to 580 °C.
Our Sales & Supplier Network
Australia, Pakistan, Malaysia, Taiwan, China, Vietnam, Belgium, Japan, South Korea, Philippines, France, United Kingdom, Indonesia, Thailand, Hong Kong, Sweden, United States, Dubai, Finland, Brunei, Germany & etc.
E Steel is the Global Metal Procurement Company in providing and sourcing raw materials to a variety of engineering industries and sectors. We work as an online B2B Metal Marketplace to help our customers in finding the required steels that are difficult to source locally.
Stainless Steel SS410 is the basic martensitic stainless steel; like most non-stainless steels it can be hardened by a “quench-and-temper” heat treatment.
Our specialty is to provide wide range of stainless steel with no minimum order (MOQ).
E Steel supply Stainless Steel SUS410 (SS410) Round Bars / Rods / Shaft , SUS410 (SS410) Plates with origin Germany and Japan.
Stainless Steel SUS410 Suppliers Singapore – SUS410 , UNS S41000 , AISI410 , DIN 1.4006 Stainless Steel
Stainless Steel SS410 is the basic martensitic stainless steel; like most non-stainless steels it can be hardened by a “quench-and-temper” heat treatment. It contains a minimum of 11.5 per cent chromium, just sufficient to give corrosion resistance properties. It achieves maximum corrosion resistance when it has been hardened and tempered and then polished. SUS410 is a general purpose grade often supplied in the hardened, but still machinable condition, for applications where high strength and moderate heat and corrosion resistance are required.Martensitic stainless steels are optimised for high hardness, and other properties are to some degree compromised. Fabrication must be by methods that allow for poor weldability and usually the need for a final heat treatment. Corrosion resistance of the martensitic grades is lower than that of the common austenitic grades, and their useful operating temperature range is limited by their loss of ductility at sub-zero temperatures and loss of strength by over-tempering at elevated temperatures.
Chemical Composition of SS410 Stainless Steel
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
SS 410 |
min.
max. |
–
0.15 |
–
1.00 |
–
1.00 |
–
0.040 |
–
0.030 |
11.5
13.5 |
– | 0.75 | – |
Mechanical Properties of SUS410 , Stainless Steel 410
Tempering Temperature (°C) | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Brinell (HB) | Impact Charpy V (J) |
Annealed * | 480 min | 275 min | 16 min | – | – |
204 | 1310 | 1000 | 16 | 388 | 30 |
316 | 1240 | 960 | 14 | 325 | 36 |
427 | 1405 | 950 | 16 | 401 | # |
538 | 985 | 730 | 16 | 321 | # |
593 | 870 | 675 | 20 | 255 | 39 |
650 | 755 | 575 | 23 | 225 | 80 |
* Annealed properties are specified for Condition A of ASTM A276, for cold finished bar.
# Due to associated low impact resistance this steel should not be tempered in the range 425-600°C
SUS410 Stainless Steel also equivalent to
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
BS | En | No | Name | ||||
SS410 | S41000 | 410S21 | 56A | 1.4006 | X12Cr13 | 2302 | SUS 410 |
* These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted.
Corrosion Resistance of SUS410 , SS410
410 Stainless Steel resists dry atmosphere, fresh water, mild alkalies and acids, food, steam and hot gases. Must be hardened for maximum heat and corrosion resistance. Performance is best with a smooth surface finish. Less corrosion resistant than the austenitic grades and also less than 17% chromium ferritic alloys such as Grade 430.
Heat Resistance of Stainless Steel AISI 410
Good resistance to scaling up to approximately 650°C, but generally not recommended for use in temperatures between 400 and 580°C, because of the reduction in mechanical properties.Heat Treatment of AISI 410 , SS410
Annealing – Grade 410 steels can be fully annealed at temperatures from 815 to 900 °C, followed by slow furnace cooling and air-cooling. Process annealing of grade 410 steels can be carried out at temperatures ranging from 650 to 760 °C and air-cooled.Hardening – Hardening of grade 410 steels can be performed at 925 to 1010 °C, followed by air and oil quenching. Heavy sections of grade 410 need to be oil quenched. Tempering, to enhance the mechanical properties and hardness of grade 410 steels, follows this process. It is not recommended to perform tempering at temperatures from 400 to 580 °C.
Applications for SUS410 Stainless Steel
Typical applications for Stainless Steel AISI 410 includes :- Bolts & Nults
- Screws
- Bushings
- Pump and valve parts and shafts
- Steam and gas turbine parts
- Petroleum fractionating towers
- Mine ladder rungs
Our Sales & Supplier Network
Australia, Pakistan, Malaysia, Taiwan, China, Vietnam, Belgium, Japan, South Korea, Philippines, France, United Kingdom, Indonesia, Thailand, Hong Kong, Sweden, United States, Dubai, Finland, Brunei, Germany & etc.
E Steel is the Global Metal Procurement Company in providing and sourcing raw materials to a variety of engineering industries and sectors. We work as an online B2B Metal Marketplace to help our customers in finding the required steels that are difficult to source locally.