JIS SUP9 Steel Rod is a high quality Cold work Spring Steel, It belong to the high quality high carbon alloy Spring Steel. Oil Quenched & Tempered Hardness is 28-34 HRc. SUP9 steel Annealing delivery hardenss less than 250HB.



Chemical Composition of SUP9 

C() 0.52-0.60 Si() 0.15-0.35 Mn() 0.65-0.95 P() ≤0.030
S() ≤0.035  Cr() 0.65-0.95        


 

SUP9 Alloy Spring Steel Equivalent to 

USA Germany China Japan France England Italy Poland ISO Austria Sweden Spain
DIN,WNr GB JIS AFNOR BS UNI PN ISO ONORM SS UNE
5155 / G51550 55Cr3 / 1.7176 55CrMnA SUP9 55C3 ≈527A60     55Cr3      


Heat treatment Related for 1.7176 Spring Steel 

  • Annealing of SUP9 Spring Steel
    Slowly heated to 740-770 and allow enough times, let the steel to be thoroughly heated, Then cool slowly in the furnace. The SUP9 tool  steel will get MAX 250 HB (Brinell hardness).

     
  • Hardening of SUP9 Spring Steel
    SUP9 steels should be heated uniformly to 830-860°C (1526-1580°F) until completely heated through. About 30 min per 25 mm of ruling section is to be provided and then the steels should be immediately quenched in oil.

     
  • Tempering of SUP9 Spring Steel
    Tempering of SUP9 steels is performed at 460-510°C, Soak well at the selected temperature and soak for at least one hour per 25mm of total thickness.

 

Mechanical Properties of SUP9 Spring Steel 

The mechanical properties of SUP9 Spring Steels are outlined in the following table.

Tensile strength Conditions to yield strength Elongation Reduction of area Hardness (Hot Rolled) Hardness (Cold Drawn)
σb (MPa)≥1225(125) σ0.2 (MPa)≥1080(110) δ5 (%)≥9 ψ (%)≥20 ≤321HB;  


Applications of SUP9 

SUP9 steels, Highlight the advantage is good hardenability, another hot working performance, comprehensive mechanical properties, Decarburization resistance is also good big cross section of various important spring, such as automobile, locomotive, large plate spring, spring, etc. SUP9 Spring main used for heavy vehicles, tractors, industrial production load, stress and the diameter of the larger plate spring and helical spring