SUP9 Spring Steel
SUP9 Spring Steel | 55CrMnA | 55Cr3 | 1.7176 | 527A60 | 55C3 | ASTM 5155
E Steel is the supplier Malaysia of Spring Steel SUP9 , we export to Singapore , Brunei , Indonesia.
JIS SUP9 Steel Rod is a high quality Cold work Spring Steel, It belong to the high quality high carbon alloy Spring Steel. Oil Quenched & Tempered Hardness is 28-34 HRc. SUP9 steel Annealing delivery hardenss less than 250HB.
Chemical Composition of SUP9
| C(£¥) | 0.52-0.60 | Si(£¥) | 0.15-0.35 | Mn(£¥) | 0.65-0.95 | P(£¥) | ≤0.030 |
| S(£¥) | ≤0.035 | Cr(£¥) | 0.65-0.95 |
SUP9 Alloy Spring Steel Equivalent to
| USA | Germany | China | Japan | France | England | Italy | Poland | ISO | Austria | Sweden | Spain |
| – | DIN,WNr | GB | JIS | AFNOR | BS | UNI | PN | ISO | ONORM | SS | UNE |
| 5155 / G51550 | 55Cr3 / 1.7176 | 55CrMnA | SUP9 | 55C3 | ≈527A60 | 55Cr3 |
Heat treatment Related for 1.7176 Spring Steel
-
Annealing of SUP9 Spring Steel
Slowly heated to 740-770 ¡æ and allow enough times, let the steel to be thoroughly heated, Then cool slowly in the furnace. The SUP9 tool steel will get MAX 250 HB (Brinell hardness).
-
Hardening of SUP9 Spring Steel
SUP9 steels should be heated uniformly to 830-860°C (1526-1580°F) until completely heated through. About 30 min per 25 mm of ruling section is to be provided and then the steels should be immediately quenched in oil.
-
Tempering of SUP9 Spring Steel
Tempering of SUP9 steels is performed at 460-510°C, Soak well at the selected temperature and soak for at least one hour per 25mm of total thickness.
Mechanical Properties of SUP9 Spring Steel
The mechanical properties of SUP9 Spring Steels are outlined in the following table.
| Tensile strength | Conditions to yield strength | Elongation | Reduction of area | Hardness (Hot Rolled) | Hardness (Cold Drawn) |
| σb (MPa)£º≥1225(125) | σ0.2 (MPa)£º≥1080(110) | δ5 (%)£º≥9 | ψ (%)£º≥20 | ≤321HB; |