SCM415 Case Harden Steel
SCM415 Case Harden Steel  Alloy Steel Malaysia, Selangor, Kuala Lumpur (KL), Klang Supplier, Suppliers, Supply, Supplies | E STEEL SDN. BHD.

SCM415 Steel Suppliers - 15CrMo5 , 1.7262 

SCM415 Round Bar is a kind of Low carbon and Cr-Mo heat treated by surface hardening process, use for gears and wear resistant parts with tough cores.

SCM415 Steel is one of the most common used low-carbon alloy steel , carbon content around 0.15% +/-.  
In general , it is carburized for use.  JIS SCM415 can be said to have higher strength compared to S45C (760 Medium Carbon Steel) or SCM440 , and surface hardness should be around 55HRC to 60HRC for use.  

 

Chemical Composition of SCM415 

Grade C Si Mn P S Ni Cr Mo
JIS G4053 SCM415 0.13-0.18 0.15-0.35 0.6-0.9 ≤0.03 ≤0.03 ≤0.25 0.9-1.2 0.15-0.25

 

Mechanical Properties of 1.7262 Steel 

Grade Delivery State T.S.
N/mm2
Min
Y.S.
N/mm2
Min
A,%
Min
Z,%
Min
Hardness,
(annealing or tempering) HB,max
Forging ratio Grain Size
(level)
Nonmetal ratio
JIS G4053 SCM415 Hot rolled, forged, or heat treatment 834 16 40 235-321 ≥ 4:1 ≥ 6 ≤ 2.0



Applications of SCM415 Alloy Steel 

SCM415 steel is a alloy structural steel. It is used for engineering structural, like high tensile shafts, bolts and nuts, gears, pinions and spindles. Locomotive traction with the big gear, supercharger drive gear, pressure vessel, rear axle, gear load of connecting rod and a spring clip,SCM415 can also be used to under 2000 m deep well of oil drill pipe joint and the fishing Alloy, and can be used for bending machine mould, etc

 

Heat Treatment of SCM415 Steel 

  • Forging Of SCM415 steel-hot work alloy Alloy steel
    Heat to 900-1100 °C(1652-2012°F)£¨forged temperature not below 843°(1550°F)

     
  • Annealing of SCM415 Alloy steel
    Slowly heated to 800~850 °ś£®1472~1562°F£© and allow enough times, let the steel to be thoroughly heated, Then cool slowly at Maximum of 4°C£®40°F£©per hours. The SCM415 Alloy  steel will get MAX 235 HB (Brinell hardness).

     
  • Hardening of SCM415 Case Harden steel
    SCM415 steels should be heated uniformly to 840-875°C (1544-1607°F) until completely heated through. If needed, the steels can be preheated at 300-500°C (572-932°F). About 30 min/per 25 mm of ruling section is to be provided and then the steels should be immediately quenched in oil.

     
  • Tempering of SCM415 Alloy steel
    Tempering of SCM415 steels is performed at 500-700°C (932-1292°F), Soak well at the selected temperature and soak for at least one hour per 25mm of total thickness. Then cool in air. Low Tempering is not advised as tempering within this range will seriously reduce the impact value. (250-375°C)

     

 

Our Sales & Supplier Network

Australia, Pakistan,  Malaysia, Singapore, Taiwan, China,Vietnam, Belgium, Japan, South Korea, Philippines, France, United Kingdom, Indonesia, Thailand, Hong Kong, China, Sweden, United States, Dubai, Finland, Brunei,Germany.

E Steel is a Global Metal Procurement Company in providing and sourcing raw materials to the wide range of engineering industries / sectors.  We works as the the Online B2B Metal Marketplace to help our customers in finding the special steels that might feel hard to source locally.  


 


Please leave your enquiry here, we will reply as soon as possible.


*only support gif, jpeg, jpg, png, pdf
Switch To Desktop Version