6587 Steel | Case Hardening Steel
6587 Steel | Case Hardening Steel  Alloy Steel Malaysia, Selangor, Kuala Lumpur (KL), Klang Supplier, Suppliers, Supply, Supplies | E STEEL SDN. BHD.

1.6587 Steel Suppliers - 18CrNiMo7-6 Case Hardening Steel 

DIN 1.6587 Steel is a low carbon,case hardening (carburizing) steel which contains 1.8% chromium – nickel – molybdenum as strengthening agents as per EN 10084. Characterised by high core strength and toughness in medium to large sections with case hardness up to Rc62 when carburized, hardened and tempered,and it is also used in area of heavy and high strained gear parts with high demands on toughness at core tensile of 1050–1350N/mm2.DIN1.6587/18CrNiMo7-6 is same as 17CrNiMo6 steel,generally supplied in the annealed condition with a maximum brinell hardness of 229 (Rc22).


Chemical Composition of 1.6587 Case Hardening Steel 
 

Standard Grade C Mn P S Si Ni Cr Mo
EN 10084 18CrNiMo7-6 0.15-0.21 0.50-0.90 ≤ 0.025 ≤ 0.035 ≤ 0.04 1.4-1.7 1.5-1.8 0.25-0.35
1.6587

 

18CrNiMo7-6 Steel Mechanical Property

Size mm ≤ 11 12-30 31-63
R Mpa 1180-1420 1080-1320 980-1270
Rp 0.2 Mpa ≥ 835 ≥785 ≥ 685
A % ≥ 7 ≥ 8 ≥ 5
C % ≥ 30 ≥ 35 ≥ 35
Kv J ≥ 44 ≥ 44  
Hardness HB 354-406 327-384 295-373

 

Forging

DIN 1.6587 | 17CrNiMo6 |18CrNiMo7-6 forging temperature:900 – 1100°C,cool slowly in the sand after forged.

 

Heat Treatment

  • Normalizing:850 – 880°C/air
  • Soft annealing:650 – 700°C/furnace
  • Stress relieve:630- 650oC
  • Carburising:880 – 980°C
  • Core hardening:830 – 870°C/water
  • Intermediate annealing:630 – 650°C
  • Case hardening:780 – 820°C/water
  • Tempering:150 – 200°C

 

Surface Hardness

  • Treated to improveshearability(+S):Max 255HB
  • Soft annealed(+A):Max 229HB
  • Treated to hardness range(+TH):179-229HB
  • Treated to ferrite-pearlite structure and hardness range(+FP):159-207HB


Application for Material 6587 Alloy Steel 

DIN 1.6587 | 17CrNiMo6 | 18CrNiMo7-6 steel for the parts which require core tensile strength and high hardness. Susceptible to the large seized parts with high wearing resistance and loading such as: Heavy Duty Bushings and Bearings, Cam Followers, Clutch Dogs, Compressor Bolts, Extractors, Fan Shafts, Heavy Duty Gears, Pump Shafts, Sprockets, Tappets, Wear Pins, Wire Guides etc..

 