H13 Tool Steel, 2344, SKD61, 8407 Hot Work Tool Steel
H13 Tool Steel, 2344, SKD61, 8407 Hot Work Tool Steel Tool Steel Malaysia, Selangor, Kuala Lumpur (KL), Klang Supplier, Suppliers, Supply, Supplies | E STEEL SDN. BHD.
We are the Supplier of H13 Tool Steel. 
AISI H13 (1.2344, SKD61) Hot Work Tool Steel air hardening, with good toughness, resistance to abrasion and high red hardness.

We supply and export to Singapore , Indonesia , Brunei and other ASEAN Countries.  
Our specialty is to provide wide range of stainless steel
 with no minimum order (MOQ).

E Steel supply H13 (2344, SKD61 Tool Steel) Round Bars / Rods / Shafts , H13 Plates.  



H13 Steel Suppliers - 1.2344, SKD61, 8407 Tool Steel 

AISI H13 Hot Work Tool Steel air hardening, with good toughness, resistance to abrasion and high red hardness. It resists softening to 550°C and has good resistance to heat checking. Will Nitride with a case hardness over 1000 V.P.N. Generally supplied annealed to HB 230 max.

Applications of 2344 Steel 

H13 Tool Steel can use for Hot punches and dies for blanking, bending, swaging and forging, hot extrusion dies for aluminium, cores, ejector pins, inserts and nozzles for aluminium, tin and lead die casting.

Chemical Compositon of SKD61, 8407 Steel 

C Si Mn Cr Mo Ni V
0.37 to 0.42 0.80 to 1.20 ≤ 0.50 4.80 to 5.50 1.20 to 1.50 0.80 to 1.20

H13 Tool Steel is also equivalent to 

Country USA German Japan
Standard ASTM A681 DIN EN ISO 4957 JIS G4404
Grades H13 1.2344/X40CrMoV5-1 SKD61

Mechanical Properties of AISI H13 Steel 

Properties Metric Imperial
Tensile strength, ultimate (@20°C/68°F, varies with heat treatment) 1200 – 1590 MPa 174000 – 231000 psi
Tensile strength, yield (@20°C/68°F, varies with heat treatment) 1000 – 1380 MPa 145000 – 200000 psi
Reduction of area (@20°C/68°F) 50.00% 50.00%
Modulus of elasticity (@20°C/68°F) 215 GPa 31200 ksi
Poisson’s ratio 0.27-0.30 0.27-0.30


Machinability 

Machinability of H13 is medium to good. It rates as 75% that of the W group water hardening tool steels which are low alloy and of generally good

Heat Treatment

Preheat to 1500 f and then heat to 1850 F. Hold at 1850 f for 15 to 40 minutes and then air cool (air quench).

Tempering each time.

Temper at 1000 F to 1200 F for Rockwell C of 53 to 38. It is advisable to do a double temper by repeating the process and use 1 hour at temperature

Hardening

May refer to “Heat Treating” and “Tempering”.


Our Sales & Supplier Network

Australia, Pakistan,  Malaysia, Singapore, Taiwan, China,Vietnam, Belgium, Japan, South Korea, Philippines, France, United Kingdom, Indonesia, Thailand, Hong Kong, China, Sweden, United States, Dubai, Finland, Brunei,Germany.


OUR MOTTO : ” WHY BUY A FULL BAR OR SHEET WHEN YOU JUST NEED A SMALL VOLUME?

Our specialty is to provide wide range of alloy steel with no minimum order.( no MOQ )



Please leave your enquiry here, we will reply as soon as possible.


*only support gif, jpeg, jpg, png, pdf
Switch To Desktop Version