2083 Plastic Mould Steel
2083 Plastic Mould Steel Plastic Mould Steel Malaysia, Selangor, Kuala Lumpur (KL), Klang Supplier, Suppliers, Supply, Supplies | E STEEL SDN. BHD.
We are the Leading Supplier of 2083 Steel. 
1.2083 Steel is Martensitic Stainless Chrome Plastic Mold Steel. 

We supply and export to Singapore , Indonesia , Brunei and other ASEAN Countries.  
Our specialty is to provide wide range of stainless steel
 with no minimum order (MOQ).

E Steel supply 2083 Steel Round Bars / Rods / Shafts , 2083 Plates with cut to size services. 




Description

1.2083 Steel Suppliers - SUS420 , AISI420

1.2083 is Martensitic Stainless Chrome Plastic Mold Steel. DIN 1.2083 is a chromium content up to 13% of the plastic die steel. 1.2083 mold steel has good polishing and excellent wear resistance, is often used to prevent acid plastic mold.

1.2083 stainless steel is generally supplied annealed condition with a hardness < 230HB. It can also be delivered ESR and quenched and tempered to 320 HB.



Characteristics of 1.2083 Mould Steel are

  • A good atmospheric corrosion resistance,
  • An excellent polishability,
  • A good machinability in annealed condition,
  • A high hardenability
  • A good wear resistance

Chemical Composition of 2083 Steel 

DIN ISO 4957 C Mn P S Si Cr
1.2083 / X40Cr14 0.36 0.42 max 1.0 0.03 0.03 max 1.0 12.50 14.50


1.2083 Steel Equivalent and Related Specifications

USA , AISI German, DIN Japan, JIS China ISO
ASTM A681 DIN 17350 JIS G4403 GB/T 9943 ISO 4957
420 Modified 1.2083/X42Cr13 SUS420 4Cr13 X42Cr13


Applications of 2083 Steel 

This steel offers very good polishing properties. Mainly used in plastic mould requiring very fine (mirror) polishing, and also for fine cutlery, surgery cutting tools and razor blades.

Heat Treatment of 1.2083 ( SUS420 )

It is recommended to use vacuum furnaces or furnaces with controlled protective gas atmosphere in order to protect the steel against oxidation and decarburization.
  • Austenitizing in a temperature range from 1000ºC to 1050ºC (not higher in order to avoid retained austenite) followed by oil quenching.
  • Heating must be performed very slowly to minimize distortion. 
     
Quenching 

It has to be performed in order to get the best microstructure, tool performance and minimum distortion. A slow quenching rate is recommended to minimize distortion but the quenching rate has to be sufficient to avoid the formation of undesirable components like bainite or ferrite / pearlite.


Tempering

It must be carried out immediately after quenching at a temperature in accordance with the mechanical properties required.
  • For high hardness (52-56HRC), temper at temperature of 200ºC for 1.5 to 2 hours.
  • For better toughness (low hardness),


Our Sales & Supplier Network

Australia, Pakistan,  Malaysia, Singapore, Taiwan, China,Vietnam, Belgium, Japan, South Korea, Philippines, France, United Kingdom, Indonesia, Thailand, Hong Kong, China, Sweden, United States, Dubai, Finland, Brunei,Germany.

E Steel is a Global Metal Procurement Company in providing and sourcing raw materials to the wide range of engineering industries / sectors.  We works as the the Online B2B Metal Marketplace to help our customers in finding the special steels that might feel hard to source locally.


 

Please leave your enquiry here, we will reply as soon as possible.


*only support gif, jpeg, jpg, png, pdf
Switch To Desktop Version